Commands list
×MENU
EXPAND ALL
SORT A-Z
- Input handling
- Solution control and techniques
- Output
-
Mesh commands
- ACTIVATE_ELEMENTS
- ADD_MASS
- CHANGE_PART_ID
- COMPONENT_BOLT
- COMPONENT_BOX
- COMPONENT_BOX_IRREGULAR
- COMPONENT_CYLINDER
- COMPONENT_PIPE
- COMPONENT_REBAR
- COMPONENT_SPHERE
- CONNECTOR_DAMPER
- MERGE_DUPLICATED_NODES
- REDISTRIBUTE_MESH_CARTESIAN
- REFINE
- SMOOTH_MESH
- SUBDIVIDE_PART_THICKNESS
- TRANSFORM_MESH_CARTESIAN
- TRANSFORM_MESH_CYLINDRICAL
- TRIM
- TRIM_HOLE
- WELD
- Nodes and connectivity
-
Material properties
- EOS_GRUNEISEN
- MAT_BB
- MAT_BERGSTROM_BOYCE
- MAT_CABLE
- MAT_CERAMIC
- MAT_CONCRETE_2017
- MAT_CONCRETE_2018
- MAT_CONCRETE_2021
- MAT_CREEP
- MAT_ELASTIC
- MAT_FABRIC
- MAT_FABRIC_ISOTROPIC
- MAT_FLUID
- MAT_FOAM
- MAT_FORMING
- MAT_FORMING_R
- MAT_GRANULAR_CAP
- MAT_HJC_CONCRETE
- MAT_HOEK_BROWN
- MAT_HOT_FORMING
- MAT_HSS
- MAT_JC
- MAT_JC_FIELD
- MAT_JH_CERAMIC
- MAT_LEE_TARVER
- MAT_LIBRARY
- MAT_METAL
- MAT_MMC
- MAT_MMC_OST
- MAT_MM_CONCRETE
- MAT_MOONEY_RIVLIN
- MAT_MULTILAYER_ORTHOTROPIC
- MAT_OBJECT
- MAT_ORTHOTROPIC
- MAT_POWDER_BURN
- MAT_REBAR
- MAT_RIGID
- MAT_USER_X
- MAT_VISCOUS_FOAM
- MAT_VISCO_PLASTIC
- MAT_YEOH
- MAT_ZA
- PROP_DAMAGE_BRITTLE
- PROP_DAMAGE_CL
- PROP_DAMAGE_CL_0_45_90
- PROP_DAMAGE_CL_ANISOTROPIC
- PROP_DAMAGE_CL_REGULARIZE
- PROP_DAMAGE_HC
- PROP_DAMAGE_IMP
- PROP_DAMAGE_IMP_ISO
- PROP_DAMAGE_JC
- PROP_DAMAGE_JC_REGULARIZE
- PROP_DAMAGE_STRAIN
- PROP_THERMAL
-
Initial conditions
- INITIAL_CONTACT
- INITIAL_DAMAGE_MAP
- INITIAL_DAMAGE_RANDOM
- INITIAL_DAMAGE_SURFACE_RANDOM
- INITIAL_MATERIAL_DIRECTION
- INITIAL_MATERIAL_DIRECTION_PATH
- INITIAL_MATERIAL_DIRECTION_VECTOR
- INITIAL_MATERIAL_DIRECTION_WRAP
- INITIAL_PLASTIC_STRAIN_FUNCTION
- INITIAL_STATE
- INITIAL_STATE_HAZ
- INITIAL_STATE_WELDSIM
- INITIAL_STRESS_FUNCTION
- INITIAL_TEMPERATURE
- INITIAL_THICKNESS
- INITIAL_VELOCITY
- REMAP
- Boundary conditions
- Loads
- Contact and tied interfaces
- Rigid bodies
- Connectors
- Parameters and functions
- Geometries
- Sets
- Coordinate system
- Particle
- CFD
- γSPH
Third-party add-ons
INITIAL_STATE_HAZ
Initial conditions
Initial conditions
*INITIAL_STATE_HAZ
entype${}_{weld}$, enid${}_{weld}$, entype${}_{base}$, enid${}_{base}$, cid${}_{sigy}$, cid${}_{D0}$
entype${}_{weld}$, enid${}_{weld}$, entype${}_{base}$, enid${}_{base}$, cid${}_{sigy}$, cid${}_{D0}$
Parameter definition
Variable | Description |
---|---|
entype${}_{weld}$ | Weld entity type |
options: P, PS | |
enid${}_{weld}$ | Weld entity ID |
entype${}_{base}$ | Base material entity type |
options: P, PS | |
enid${}_{base}$ | Base material entity ID |
cid${}_{sigy}$ | ID of a CURVE or FUNCTION describing yield stress as function of the distance from the weld |
default: not used | |
cid${}_{D0}$ | ID of a CURVE or FUNCTION describing initial damage as function of the distance from the weld |
default: not used |
Description
This command is used to define mechanical properties in a HAZ after a welding operation. Initial yield stress and damage are defined as functions of the distance from the weld. The yield stress can be accessed in FUNCTION through the built in variable sigy0.